Ballistic electron emission microscopy of strained and relaxed In0.35Ga0.65As/AlAs interfaces

Ke, Mao-long, Westwood, David I., Wilks, S., Heghoyan, S., Kestle, A., Matthai, Clarence Cherian, Richardson, Bernard E. and Williams, R. H. 1995. Ballistic electron emission microscopy of strained and relaxed In0.35Ga0.65As/AlAs interfaces. Journal of Vacuum Science & Technology B: Microelectronics and Nanometer Structures 13 (4) , p. 1684. 10.1116/1.587878

Full text not available from this repository.

Abstract

We report here our investigations upon both strained and relaxed In0.35Ga0.65As/AlAs interfaces using the ballisticelectron emissionmicroscopy (BEEM) and current–voltage (I–V) techniques. Six samples, of different InGaAs thickness and doping density, were grown by molecular beam epitaxy and were designed to assess the importance of strain relaxation/dislocations in barrier formation. In the heavily dislocated situation (thicker InGaAs film) the obtained barrier most likely resulted from Fermi level pinning. However, this was obviously not the case for both the pseudomorphic and lightly dislocated situations (thinner InGaAs films). It was also noted that the measured barriers varied more widely over space in the lightly dislocated layer than that in the pseudomorphic case and that the simultaneously obtained topographic and BEEM images points to a better interface in the pseudomorphic layer than that in the partially relaxed situation

Item Type: Article
Date Type: Publication
Status: Published
Schools: Physics and Astronomy
Subjects: Q Science > QC Physics
Publisher: American Institute of Physics
ISSN: 0734211X
Last Modified: 17 Jun 2019 02:50
URI: http://orca.cf.ac.uk/id/eprint/64959

Citation Data

Cited 8 times in Google Scholar. View in Google Scholar

Cited 11 times in Scopus. View in Scopus. Powered By Scopus® Data

Actions (repository staff only)

Edit Item Edit Item