Estimation of the yield stress and distribution of large aggregates from slump flow test of self-compacting concrete mixes using smooth particle hydrodynamics simulation

Badry, Firas, Kulasegaram, Sivakumar ORCID: https://orcid.org/0000-0002-9841-1339 and Karihaloo, Bhushan ORCID: https://orcid.org/0000-0003-0657-2678 2016. Estimation of the yield stress and distribution of large aggregates from slump flow test of self-compacting concrete mixes using smooth particle hydrodynamics simulation. Journal of Sustainable Cement-Based Materials 5 (3) , pp. 117-134. 10.1080/21650373.2014.979266

Full text not available from this repository.

Abstract

A wide range of normal strength self-compacting concrete (SCC) mixes with a maximum aggregate size (g) of 20 mm ranging in compressive strength from 30 to 80 MPa were prepared in the laboratory, and the times t500 and tstop of each mix were recorded in the slump flow test. The entire cone flow test was then simulated from the moment the cone was lifted until the mix stopped to flow using the three-dimensional mesh-less smoothed particle hydrodynamics computational approach, treating the SCC mix as a non-Newtonian Bingham fluid. This numerical simulation had two aims. First, to investigate whether the yield stress τy of the mix could be accurately estimated from the measured t500 and tstop times knowing the plastic viscosity of the mix. The latter was estimated by a micromechanical procedure. Second, to compare the distribution of coarse aggregate particles larger than or equal to 8 mm in the cone spread after it stopped to flow as revealed by the numerical simulation with the distribution of the aggregate particles of the corresponding sizes in the cut sections of the cured test cone spread. The large coarse aggregate particles in the size ranges (8 ≤ g < 12, 12 ≤ g < 16, 16 ≤ g < 20 and g ≥ 20 mm) of the test SCC mixes were color coded with non-toxic non-water soluble paints so that the outlines of the aggregate particles could be clearly distinguished in the cut sections of the hardened cone spread and compared with the numerical simulations. It is shown that both aims of the investigations were successfully attained.

Item Type: Article
Date Type: Publication
Status: Published
Schools: Engineering
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
Publisher: Taylor & Francis
ISSN: 2165-0373
Date of Acceptance: 16 October 2014
Last Modified: 28 Oct 2022 08:47
URI: https://orca.cardiff.ac.uk/id/eprint/72123

Citation Data

Cited 13 times in Scopus. View in Scopus. Powered By Scopus® Data

Actions (repository staff only)

Edit Item Edit Item